摘要：pH=10的柠檬酸铵一氨水溶液中，钴与苦氨酸偶氮变色酸反应形成绿色配合物，其最大吸收波长为650 nlTl，表观摩尔吸光系数为2．62×104 L／(mol·cm)。在25 mL溶液中，钴含量在0～50Ix9范围内遵循比尔定律。样品分析表明，该法的相对标准偏差小于2％。 关键词：锡钴合金；镀液；钴；测定；苦氨酸偶氮变色酸；分光光度法 中图分类号：T0657．32 文献标志码：A 文章编号：1004—227X(2009)05—0035—02 Speetrophotometric determination of cobalt in tin-cobalt ahoy plating solution with picramazochrom//ZHONG Guo-xiu+，YANG Hao-yi，YAN Ga0—hua Abstract：Cobalt reacts with picramazochrom to form a green complex with a apparent molar absorption coefficient．of 2．62×104L／(mol·cm)at the wavelength of 650 nlTI in a solution consisting of ammonium citrate and ammonia at pH 10．Beer’S law is obeyed in the range of0—50μg cobalt in a 25 mL bath．Sample analysis showed that the relative standard deviation was less than 2％． Keywords：tin——cobalt alloy；plating bath；cobalt；determination；picramazochrom；spectrophotometry First-author’S address：Hubei Reserch&Design Institute ofMechanical Electronic Engineering，Wuhan 430070，China
1 前言
锡钻合金镀层具有优良的耐蚀性和抗变色性，较高的硬度和较低的内应力，镀层基本无空隙，覆盖能力优良，因此在滚镀方面可代替操作要求苛刻的滚镀铬，并已应用于无耐磨要求的代铬镀层[1-2]。镀层中钻含量在20％左右时，镀层外观接近铬；钴含量低于20％时，镀层呈光亮的白色；钴含量高于20％时，外观为枪黑色或黑色。因此，生产中监测镀液中钴含量的高低具有重要意义。
锡钴合金镀液中钻的测定方法主要有分光光度法[3-4]、滴定法[5]等。苦氨酸偶氮变色酸已用于测定钢铁[6]及铝合金[7]中的钴含量，本文尝试将其应用于锡钴镀液中钴的测定。同时，以柠檬酸铵一氨水溶液作为显色介质并掩蔽其他共存元素(尤其是铁)的干扰，收到了较好的效果。该法简单快速，结果准确可靠。
分光光度法测定锡钻合金镀液中的钴：实验 分光光度法测定锡钻合金镀液中的钴：结果与讨论 分光光度法测定锡钻合金镀液中的钴：结论
|