摘要：在纯锌浴中添加钛，制得锌—钛合金镀层含硅钢板。通过塔菲尔极化及电化学阻抗测量，研究了其在w=5％的NaCI水溶液中的腐蚀电化学行为，并与热浸纯锌镀层钢板进行了对比。结果表明，锌—钛合金镀层钢板的极化电阻和交流阻抗增大，腐蚀电流密度减小，耐蚀性能得到提高。
关键词：含硅钢；锌—钛合金镀层；热浸镀；耐蚀性；电化学
中图分类号：TQl53．2 文献标志码：A
文章编号：1004—227X(2009)03—0021一03
Electrochemical behavior of hot-dip zinc-tanium alloy galvanized steel sheet／／GUI Yan，XU Qia0—yu*
Abstract：A Zn—-Ti galvanizing coating was prepared on Si-containing low--carbon steel by hot--dip galvanizing in a Zn—Ti bath．The corrosion performance and electrochemical behavior of Zn and Zn-Ti alloy galvanized steel sheets in 5％一(mass fractionl NaCl solution were studied by Tafel polarization and electrochemical impedance spectroscopy fEIS)．The results showed that the hot．dip Zn-Ti galvanized steel sheet has higher polarization resistance and electr0．chemical impedance but lower corrosion current density as compared with the hot．dip Zn galvanized one。The corrosion resistance of Zn-Ti galvanized steel sheet was improved．
Keywords：silicon．．containing low．．carbon steel；zinc—— titanium alloy coating；hot-dip galvanizing；corrosion resistance；electrochemistry
First-author’s address：Panyu Polytechnic，Guangzhou 51 1483．China
1 前言
热浸锌作为钢铁材料表面防护工艺之一，在交通、建筑、通讯、电力等领域获得了广泛的应用[1-3]。在锌浴中添加合金元素形成的热浸锌合金镀层，具有较好的腐蚀保护作用，常用的有Ni、Mn、Al、Mg等。锌浴中添加各种合金元素以后，主要有以下几方面的作用：(1)利用合金化，使金属表面形成热力学稳定性高的连续保护层，耐蚀性提高；(2)提高镀层的阴极极化度，降低腐蚀速率；(3)降低阳极活性，尤其是提高金属的钝性来减缓阳极反应过程；(4)形成完整的腐蚀产物保护膜，加入一些能促使表面生成致密保护膜的合金元素，提高腐蚀体系电阻，减缓腐蚀过程。
钛是一种高钝态性的金属，易钝化，同时有很强的钝态稳定性。在大气或水溶液中，钛表面会立即形成一层保护性能很好的氧化膜，使之处于钝态。钛不仅可在含氧的溶液中保持稳定钝态，在含有任何浓度的氯离子溶液中也保持钝态[4]。本文以钛作为添加元素，研究了含硅钢在不同钛含量的液态锌中热浸镀后获得的镀层的耐蚀性能。
|